ETI Injection Epoxy


Restoration Products

This product's information may differ depending on the category of use. You are currently viewing details related to Restoration Products. You can also view product information related to the category: Cartridge Solutions

ETI injection epoxies are two-component, high-solids formulations for the injection into cracks in concrete. Dispensed through a static mixing nozzle using either a manual, battery-powered or a pneumatic dispensing tool, these epoxies provide a waterproof, high strength (structural) repair.

Key Features

  • Bonds chemically to concrete, providing structural repair (meets the requirements of ASTM C 881 for structural repair epoxy)
  • Formulated for maximum penetration under pressure (all viscosities)
  • Seals out moisture, protecting rebar in the concrete from corrosion and flooring from moisture damage
  • Reliable mixing and ratio control when used with the Simpson Strong-Tie® Optimix® static mixing nozzle (included with cartridge)
  • Suitable for pressure injection or gravity-feed applications
  • Non-shrink material resists oils, salts and mild chemicals
  • Final product color: ETI-SLV – dark purple / black; ETI-LV – amber; ETI-GV – gray

ETI-SLV Super-Low-Viscosity Epoxy

  • Super-low viscosity (350 cP) repairs hairline cracks (0.002") and cracks up to 1/4" in width
  • Penetrates smallest cracks
  • Meets or exceeds AASHTO M-235 and ASTM C881 Type I and IV, Grade 1, Class B and C

ETI-LV Low-Viscosity Epoxy

  • Repairs fine to medium cracks 1/64" to 1/4" in width
  • Offers low surface tension to effectively penetrate narrow cracks
  • Approved under NSF/ANSI standard 61
  • Meets or exceeds AASHTO M-235 and ASTM C881 Type I and IV, Grade 1, Class C

ETI-GV Gel-Viscosity Epoxy

  • Gel-viscosity (non-sag) epoxy repairs medium cracks 3/32" – 1/4" in width
  • Decreases in viscosity under pressure, increasing flow
  • Suitable for use as pick-proof sealant around doors, windows and fixtures
  • Meets or exceeds AASHTO M-235 and ASTM C881 Type I and IV, Grade 3, Class C
Model No. Option Carton Qty.
ETIGV22 ETI-GV Gel-Viscosity Cartridge System, 22 oz. 10
ETIGVKT2 ETI-GV Gel-Viscosity Epoxy Bulk Kit, 2 gal.
ETILV22 ETI-LV Low-Viscosity Cartridge System, 22 oz. 10
ETILVKT2 ETI-LV Low-Viscosity Injection Epoxy Bulk Kit, 2 gal.
ETILVKT4 ETI-LV Low-Viscosity Injection Epoxy Bulk Kit, 4 gal.
ETISLV ETI-SLV Super-Low-Viscosity Cartridge System, 16.5 oz. 10
ETISLVKT15 ETI-SLV Super-Low-Viscosity Injection Epoxy Bulk Kit, 15 gal.
ETISLVKT150 ETI-SLV Super-Low-Viscosity Injection Epoxy Bulk Kit, 150 gal.
ETISLVKT3 ETI-SLV Super-Low-Viscosity Injection Epoxy Bulk Kit, 3 gal.


  • Suitable for repairing non-moving cracks in concrete walls, floors, slabs, columns and beams.
  • ETI can be used to inject cracks in damp or wet conditions (non-seeping or non-leaking conditions only) with excellent results.
  • Apply to concrete 60°F or above. For best results, warm material to 60°F or above prior to application.
  • Mixed material in nozzle and injection fitting hardens in 15 minutes (ETI-SLV), and in 60 minutes (ET-LV, ETI-GV) at temperatures of 40°F or above


ETI-SLV – dark purple / black; ETI-LV – amber; ETI-GV – gray

Storage Conditions

For best results, store between 45°F and 95°F

Shelf Life

24 months from date of manufacture in unopened cartridge


Use only appropriate Simpson Strong-Tie® mixing nozzles in accordance with Simpson Strong-Tie instructions. Modification or improper use of mixing nozzle may impair epoxy performance.

Clean Up

Removal of cured adhesive – Chip or grind off surface. Uncured Adhesive – Wipe up with cotton cloths. If desired, scrub area with abrasive, waterbased cleaner and flush with water. If approved, solvents such as ketones (MEK, acetone, etc.), lacquer thinner, or adhesive remover can be used. DO NOT USE SOLVENTS TO CLEAN ADHESIVE FROM SKIN. Take appropriate precautions when handling flammable solvents. Solvents may damage surface to which they are applied.

Test Data

Property Test Method ETI-SLV Results* ETI-LV Results* ETI-GV Results*
*Material and curing conditions: 73 ± 2˚F, unless otherwise noted.
Viscosity (75°F) ASTM D2556 350 cP 1,790 cP Non-sag gel
Bond Strength (moist cure) @ 2 days ASTM C882 3,100 psi 2,500 psi 1,110 psi
Bond Strength (moist cure) @ 14 days 3,900 psi 2,530 psi 3,990 psi
Tensile Strength ASTM D638 10,200 psi 7,470 psi
Tensile Elongation at Break ASTM D638 2.1% 4.8%
Compressive Yield Strength ASTM D695 16,500 psi 12,500 psi 11,600 psi
Compressive Modulus ASTM D695 569,000 psi 342,000 psi 403,000 psi
Heat Deflection Temperature ASTM D648 140°F 130°F 131°F
Water Absorption (24-hour soak) ASTM D570 0.25% 0.76% 0.58%
Linear Coefficient of Shrinkage ASTM D2556 0.0035 0.0040 0.0000
Gel Time (60-gram mass) ASTM C881 16 min. 68 min. 135 min.
Volatile Organic Compounds (VOC) EPA Method 24
ASTM D2369
23 g/L 6 g/L 4 g/L
Initial Cure 24 hours 24 hours 24 hours
Mixing Ratio by Volume (Part A:Part B) 2:1 1:1 1:1